Titanijevi kovinski materialihave shown broad application prospects in many fields such as aerospace, biomedicine, and chemical industry due to their remarkable characteristics such as high specific strength, high yield strength ratio, high deformation resistance, and good process plasticity. However, there are still deficiencies in the current research on the hot rolling process of small-diameter titanium tubes, as well as the heat treatment and microstructure analysis of rolled Vrstice . Naslednje bodo analizirale postopek valjanja in zmogljivost kovinskih materialov iz titanov podrobno z vidikov kotalne temperature, mikrostrukture valjanih izdelkov in razmerjem med postopkom valjanja in zmogljivostjo .
1. Optimizacija hitrosti valjanja in hitrosti napetosti
S celovite perspektive zmanjšanja odpornosti deformacije, izboljšanja oblikovanja in zagotavljanja končne učinkovitosti strukture je bila določena ustrezna valjasta temperatura titanove cevi 950 stopinj . ta temperatura je nekoliko nižja od fazne prehodne temperature titanove zlitine ., ki se lahko deformatizirajo debelacijsko upornost in učinkovito uravnoteženje na tej temperaturi. Roka, ustrezna temperatura lahko zmanjša deformacijsko upornost materiala, naredi postopek valjanja bolj gladko, zmanjša porabo energije opreme in obrabo valja; Po drugi strani pa lahko zagotovi, da material ohranja dobro plastičnost med postopkom valjanja, ki je naklonjena pridobivanju idealne organizacijske morfologije in uspešnosti . hkrati pa je ustrezna hitrost seva, ki vpliva Hitrost obremenitve in napetosti med deformacijo je majhna, material pa lahko v celoti igra plastičnost, s čimer pridobi enakomerno strukturo in dobre mehanske lastnosti . razumna hitrost seva pomaga pri nadzoru dinamičnega rekristalizacijskega procesa materiala, izpopolnitev zrn in izboljša trdnost in žilavost materiala .
{{0 {
Tri-roll Y-Type Rolling Mill je bil uporabljen za uspešno pridobivanje srednje velikih palic z premerom 12 mm in 6 mm . Mikrostrukture teh dveh različnih specifikacij cevi so bile opažene in analizirane, in ugotovili so, da so bile očitne razlike v njihovih mikrostrukturi za njihovo 12MM . za srednje 12-ih . phase pipe transformation structure with a grain diameter of about 3-10μm. This equiaxed structure has good isotropy and can provide relatively uniform mechanical properties in different directions. The structure of the medium 6mm pipe is composed of a small amount of equiaxed primary phase, thin strip phase and transformation structure, and the grain size is less than 1μM . Za primerjavo je razvidno, da se s povečanjem kumulativne deformacije velikost zrn znatno zmanjša ., ker med postopkom valjanja lahko večja deformacija spodbudi dinamično rekristalizacijo materiala in rafinira, vendar pa tudi zrn, ki pa tudi zrn in tudi rafinacijo zrn .}}}}}}}}}}} žilavost in še naprej izboljšajo celovito delovanje gradiva .
3. Preverjanje skladnosti procesa valjanja in uspešnosti izdelka
After comprehensive testing and analysis of the organization and mechanical properties of the hot-rolled titanium tube on the three-roll Y-type rolling mill, the results show that its organization and mechanical properties meet the technical requirements. This fully proves that the rolling equipment, rolling process parameters and heat treatment system used in the test are scientific and reasonable, and can produce titanium tube products with stable quality and excellent Zmogljivost . Ta rezultat Raziskave ponuja trdno tehnično podlago za nadaljnjo spodbujanje industrijske proizvodnje kovinskih materialov iz titanijevega, kar bo pomagalo izboljšati učinkovitost proizvodnje, zmanjšati proizvodne stroške in spodbujati široko uporabo kovinskih materialov iz titanijevih
In summary, through in-depth research on the rolling process and performance of titanium metal materials, we have identified the appropriate rolling temperature and strain rate, mastered the microstructural characteristics of pipes of different specifications, and verified the conformity of the rolling process with product performance. These research results are of great significance for optimizing the rolling process of titanium metal materials and improving product quality and performance, and will inject new impetus into Razvoj industrije kovinskih materialov iz titanov .
Nicole
Podjetje: Baoji Jimiyun Dynamic Co ., Ltd
Država: Kitajska
Dodaj: Baoti Road, Jintai, Baoji City, Shaanxi, Kitajska
Cel: +86 13369210920
Gmail: nicole@jmyunti.com
Spletna stran: www . jm-titanium . com